| Brass Wire Mesh |
| Brass wire mesh and phosphor bronze wire mesh are frequently used as sieving and filtering materials in screening pellet, powder, porcelain clay and glass, chinaware printing,filtering liquid and gas.Brass wire mesh and wire cloth possess greater strength than copper wire mesh or bronze wire mesh.Copper wire cloth finds wide usage in traveling water screens, radio frequency interference shielding, sugar and marine applications.For more information about brass woven wire mesh and wire cloth products, please contact us. |
|
|
mesh |
Wire Dia. (MM) |
Opening(mm) |
SWG |
mm |
inch |
6mesh |
22 |
0.711 |
0.028 |
3.522 |
8mesh |
23 |
0.610 |
0.024 |
2.565 |
10mesh |
25 |
0.508 |
0.020 |
2.032 |
12mesh |
26 |
0.457 |
0.018 |
1.660 |
14mesh |
27 |
0.417 |
0.016 |
1.397 |
16mesh |
29 |
0.345 |
0.014 |
1.243 |
18mesh |
30 |
0.315 |
0.012 |
1.096 |
20mesh |
30 |
0.315 |
0.0124 |
0.955 |
22mesh |
30 |
0.315 |
0.0124 |
0.840 |
24mesh |
30 |
0.315 |
0.0124 |
0.743 |
26mesh |
31 |
0.295 |
0.0116 |
0.682 |
28mesh |
31 |
0.295 |
0.0116 |
0.612 |
30mesh |
32 |
0.247 |
0.011 |
0.573 |
32mesh |
33 |
0.254 |
0.010 |
0.540 |
34mesh |
34 |
0.234 |
0.0092 |
0.513 |
36mesh |
34 |
0.234 |
0.0092 |
0.472 |
38mesh |
35 |
0.213 |
0.0084 |
0.455 |
40mesh |
36 |
0.193 |
0.0076 |
0.442 |
42mesh |
36 |
0.193 |
0.0076 |
0.412 |
44mesh |
37 |
0.173 |
0.0068 |
0.404 |
46mesh |
37 |
0.173 |
0.0068 |
0.379 |
48mesh |
37 |
0.173 |
0.0068 |
0.356 |
50mesh |
37 |
0.173 |
0.0068 |
0.335 |
60X50mesh |
36 |
0.193 |
0.0076 |
- |
60X50mesh |
37 |
0.173 |
0.0068 |
- |
60mesh |
37 |
0.173 |
0.0068 |
0.250 |
70mesh |
39 |
0.132 |
0.0052 |
0.231 |
80mesh |
40 |
0.122 |
0.0048 |
0.196 |
90mesh |
41 |
0.112 |
0.0044 |
0.170 |
100mesh |
42 |
0.012 |
0.004 |
0.152 |
120X108mesh |
43 |
0.091 |
0.0036 |
- |
120mesh |
44 |
0.081 |
0.0032 |
0.131 |
140mesh |
46 |
0.061 |
0.0024 |
0.120 |
150mesh |
46 |
0.061 |
0.0024 |
0.108 |
160mesh |
46 |
0.061 |
0.0024 |
0.098 |
180mesh |
47 |
0.051 |
0.002 |
0.090 |
200mesh |
47 |
0.051 |
0.002 |
0.076 |
|
| |
|